HiPco™ CNT Prices
Item0.5 g1.0 g
HiPCO$549
$899


HiPco™ carbon nanotubes are synthesized using high-pressure carbon monoxide process. Unlike other methods in which the metal catalysts are deposited or embedded on the substrate before carbon deposition begins, catalyst is introduced in gas phase in this method. Both the catalyst precursor and the carbon monoxide gas are fed into a furnace, followed by catalytic reaction in the gas phase. This method is highly industrializable and suitable for large-scale synthesis, because the nanotubes are free from catalytic supports and the reaction can be operated continuously. The targeted price will be as cheap as multiwalled CNTs as Atom is currently scaling up the production.


The buckypaper made of HiPco™ was reported to have sheet resistance as low as 0.2-2 Ohms/sq, and was fabricated as electrodes for LCD displays and electrophoretic displays. 


HiPco™ is the only CNTs from which single-chirality, single-walled CNT can be extracted by various separation methods. HiPco™ possesses the following advantages over CVD or arc-discharge CNTs:
• Less defects
• Stronger tubes
• More suitable for semiconductor applications.


Atom NanoElectronics Inc. is the exclusively licensed entity to manufacture, distribute and sell HiPco™ materials. 

HiPco™ carbon nanotubes are available in kg quantities for research and development.

We also provide purified and functionalized HiPco™ materials.

Please contact us using the form below or email to sales@atomnanoelectronics.com for quotes and further information. 

HiPco™ CNT Physical Properties
Individual SWCNT Diameter
~0.7 – 1.2 nm
Individual SWCNT Length
~100 – 5000 nm
Calculated Molecular Weight
~3.0x10e5 – 2.6x10e7 Amu
Color
Black
Morphology
Dry loose powder of bundled nanotubes 
Maximum Density
1.6 g/cm3
Bulk Density
~0.1 g/cm3

TGA Residue as Fe
    -Raw   

    -Pure


<35 wt%

<15 wt%

TGA 1st Derivative Peak Temperature

Raw     ~350 – 410 °C

Pure    ~350 – 410 °C

TGA Onset Temperature
Raw     ~350 °C
Pure    ~440 °C
Maximum Surface Area
1315 m2/g
BET Surface Area
~400 – 1000 m2/g
Buckypaper Resistance
0.2 – 2 Ω
Moisture Content
<5 wt%